Electroluminescent device

ABSTRACT

An optical device comprising an anode, a cathode, an organic semiconducting material between the anode and the cathode, and an electron transport layer between the cathode and the organic semiconducting material wherein the organic semiconducting material comprises sulfur and the electron transport layer containing barium.

FIELD OF THE INVENTION

[0001] The invention relates to cathodes for optical devices, in particular organic electroluminescent and photovoltaic devices.

BACKGROUND OF THE INVENTION

[0002] One class of opto-electrical devices is that using an organic material for light emission or as the active component of a photocell or photodetector (a “photovoltaic” device). The basic structure of these devices is a semiconducting organic layer sandwiched between a cathode for injecting or accepting negative charge carriers (electrons) and an anode for injecting or accepting positive charge carriers (holes) into the organic layer.

[0003] In an organic electroluminescent device, electrons and holes are injected into the semiconducting organic layer where they combine in to generate excitons that undergo radiative decay. In WO 90/13148 the organic light-emissive material is a polymer, namely poly(p-phenylenevinylene) (“PPV”). Other light emitting polymers known in the art include polyfluorenes and polyphenylenes. In U.S. Pat. No. 4,539,507 the organic light-emissive material is of the class known as small molecule materials, such as (8-hydroxyquinoline) aluminium (“Alq3”). In a practical device one of the electrodes is transparent, to allow photons to escape the device.

[0004] A organic photovoltaic device has the same construction as an organic electroluminescent device, however charge is separated rather than combined as described in, for example, WO 96/16449.

[0005]FIG. 1 illustrates the cross-sectional structure of a typical organic light-emissive device (“OLED”). The OLED is typically fabricated on a glass or plastic substrate 1 coated with a transparent first electrode 2 such as indium-tin-oxide (“ITO”). A layer of a thin film of at least one electroluminescent organic material 3 covers the first electrode. Finally, a cathode 4 covers the layer of electroluminescent organic material. The cathode is typically a metal or alloy and may comprise a single layer, such as aluminium, or a plurality of layers such as calcium and aluminium. Other layers can be added to the device, for example to improve charge injection from the electrodes to the electroluminescent material. For example, a hole injection layer such as poly(ethylene dioxythiophene)/polystyrene sulfonate (PEDOT-PSS) or polyaniline may be provided between the anode 2 and the electroluminescent material 3. When a voltage is applied between the electrodes from a power supply one of the electrodes acts as a cathode and the other as an anode.

[0006] The nature of the electrodes has a strong influence on the efficiency, and also lifetime, of the device. For the cathode electrode a number of materials have been proposed, with materials having a low work-function being generally preferred. The inclusion of a high dipole dielectric layer between the cathode and the electroluminescent layer has been shown to improve device efficiency by assisting electron injection. For example, EP 0822603 discloses a thin fluoride layer between the EL layer and a thick conductive layer. The fluoride can be selected from the group of alkali fluorides and alkali earth fluorides. The conductive layer can be selected from the group of elemental metals, metal alloys and conductive materials. For the fluoride layer thicknesses in the range 0.3 to 5.0 nm are taught. Similarly, Applied Physics Letters 79(5), 2001, 563-565 discloses metal fluoride/Al cathodes. In addition, WO 00/48257 describes an arrangement comprising a metal fluoride layer, a layer of calcium and a layer of aluminium.

[0007] A focus in the field of OLEDs has been the development of full colour displays utilising organic red, green and blue (RGB) electroluminescent materials. To this end, a large body of work has been reported in the development of both small molecule and polymeric red, green and blue emitters. These emitters comprise aromatic moieties which may carry substituents. Appropriate selection of the aromatic moiety, and/or the substituents therefor, enables tuning of the colour of emission. Electroluminescent materials comprising sulfur, such as polymers comprising thiophene or benzothiadiazole repeat units, have been reported. For example, red and green emitters comprising these units are disclosed in WO 00/46321.

[0008] Full colour OLEDs have been disclosed in, for example, Synthetic Metals 111-112 (2000), 125-128. A difficulty with these devices is poor overall device performance (i.e. efficiency, lifetime, etc.) resulting from incompatibility of the cathode with at least one of the red green and blue emitters. For example, the cathode disclosed in Synthetic Metals 111-112 (2000), 125-128 is LiF/Ca/Al which is particularly efficacious with respect to the blue emissive material but which shows poor performance with respect to green and, especially, red emitters. A particular problem of degradation in green and red efficiency has been observed when pixels of these colours are not driven.

[0009] The present inventors have identified deleterious interactions between the cathode and sulfur containing materials in the aforementioned devices. In addition to the deleterious effect of this interaction on an OLED, the same deleterious interaction will affect the semiconducting properties of the organic material in an organic photovoltaic device. It is therefore a purpose of the invention to provide a cathode that has improved compatibility with organic semiconducting materials comprising sulfur. It is a further purpose of the invention to provide a cathode which has improved compatibility with all of red, green and blue electroluminescent organic semiconducting materials.

SUMMARY OF THE INVENTION

[0010] In a first aspect, the invention provides an optical device comprising

[0011] an anode

[0012] a cathode

[0013] an organic semiconducting material between the anode and the cathode and

[0014] an electron transport layer between the cathode and the organic semiconducting material

[0015] wherein the organic semiconducting material comprises sulfur and the electron transport layer comprises barium.

[0016] In one preferred embodiment of the first aspect of the invention, the optical device is an electroluminescent device, more preferably a display device. In a second preferred embodiment of the first aspect of the invention, the optical device is a photovoltaic device.

[0017] In a second aspect, the invention provides an optical device comprising an anode, a cathode, red, green and blue electroluminescent organic semiconducting materials located between the anode and the cathode and an electron transport layer located between the electroluminescent organic semiconducting materials and the cathode wherein the electron transport layer comprises barium.

[0018] In one preferred aspect, the electron transport layer comprises elemental barium as a major component. In this aspect, the electron transport layer may be regarded as a further component of the cathode since it is a conductive material. In another preferred aspect, the electron transport layer comprises a dielectric barium compound as a major component. Preferred dielectric barium compounds include barium halides and barium oxide, most preferably barium fluoride. Preferably the layer comprising barium has a thickness in the range of 1-6 nm.

[0019] Without wishing to be bound by any theory, it is believed that when a sufficiently thin dielectric layer is used, the properties of the overlying cathode layer can influence charge injection from the cathode into the emissive layer, there is an opportunity to select materials for the cathode such that by a combination of their properties the performance of the device can be enhanced. Possible mechanisms for this enhancement are believed to include: (a) prevention by the dielectric layer of adverse interactions between the organic layer(s) and the cathode, whilst retaining at least some of the injection properties of the material of the cathode; and (b) the formation by the dielectric layer (e.g. with the organic layer or layers) of intermediate states that aid electron injection from the cathode. The dielectric layer should be sufficiently thin to allow the effect to occur but sufficiently thick that it can be deposited reproducibly and uniformly (without excessive defects). In general, possible mechanisms giving rise to improved performance include surface induced dipoles, modified work functions, charge transfer formation of chemically stable compounds and dissociation of the compound layer of the cathode to form a doped injection layer.

[0020] The or each organic semiconducting material may be a small molecule but is preferably a polymer. Examples of such materials include homopolymers and copolymers of optionally substituted poly(phenylene vinylenes) and optionally substituted polyfluorenes. Copolymers are particularly preferred. The organic semiconducting material may comprise, for example, triarylamines or heterocycles, in particular sulfur containing heterocycles. In one embodiment, the organic semiconducting material is a polymer comprising heterocyclic repeat units selected from optionally substituted 4,7-linked benzothiadiazole, 2,5-linked thiophene and combinations thereof

[0021] The cathode may consist of a single layer of conductive material, in particular a metal such as aluminium or an alloy. Alternatively, the cathode may comprise more than one layer of conductive material, in particular the cathode may be a bilayer comprising two metals of differing work functions. In a first embodiment, the cathode comprises a layer of aluminium. Preferably, the layer of aluminium has a thickness in the range of 200 to 700 nm. In a second embodiment, the cathode comprises a bilayer of calcium and aluminium wherein the layer of calcium is in contact with the layer of dielectric material. Preferably, the calcium layer has a thickness of 5-25 Å.

[0022] Preferably, a hole injecting layer comprising PEDOT:PSS is located between the anode and the semiconducting material.

[0023] By “red electroluminescent organic semiconducting material” is meant an organic material that by electroluminescence emits radiation having a wavelength in the range of 600-750 nm, preferably 600-700 nm, more preferably 610-650 nm and most preferably having an emission peak around 650-660 nm.

[0024] By “green electroluminescent organic semiconducting material” is meant an organic material that by electroluminescence emits radiation having a wavelength in the range of 510-580 nm, preferably 510-570 nm.

[0025] By “blue electroluminescent organic semiconducting material” is meant an organic material that by electroluminescence emits radiation having a wavelength in the range of 400-500 nm, more preferably 430-500 nm.

[0026] By “major component” of the electron transport layer is meant a component comprising 50-100%, preferably more than 90%, most preferably substantially all, of the electron transport layer.

BRIEF DESCRIPTION OF THE DRAWINGS

[0027] The present invention will now be described in further detail, by way of example only, with reference to the accompanying drawings in which:

[0028]FIG. 1 shows a prior art electroluminescent device

[0029]FIG. 2 shows an electroluminescent device according to the examples

[0030]FIG. 3 shows a plot of current density vs. bias for a red electroluminescent device

[0031]FIG. 4 shows a plot of current density vs. bias for a green electroluminescent device

[0032]FIG. 5 shows a plot of luminance vs. time for a red electroluminescent device

[0033]FIG. 6 shows a plot of luminance vs. time for a green electroluminescent device

[0034]FIG. 7 shows a plot of luminance vs. time for a blue electroluminescent device

EXAMPLES

[0035] A) Monochrome Electroluminescent Devices

[0036] The following examples describe the preparation of electroluminescent devices wherein the electroluminescent material comprises sulfur and the cathode comprises a barium halide layer for the purpose of comparison with corresponding devices not having a layer comprising barium.

[0037]FIG. 2 shows an organic light-emissive device according to the examples. The device comprises a transparent glass or plastic substrate 5. Over the substrate is a transparent anode electrode 6 formed of ITO. Over the anode is hole injecting layer 7 of poly(ethylene dioxythiophene)/polystyrene sulfonate (PEDOT-PSS). Over the hole injecting layer is organic light-emissive material 8 and over that is a dielectric electron transport layer 9 of barium fluoride capped with a cathode 10 comprising a layer of calcium 11 and a layer of aluminium 12.

[0038] To form the device of FIG. 2 a transparent layer of ITO to form the anode 6 is deposited on a sheet of glass 5. The glass sheet could be a sheet of sodalime or borosilicate glass having a thickness of, for instance, 1 mm. The thickness of the ITO coating is suitably around 100 to 150. The substrate 5 and the anode electrode 6 may be a pre-prepared commercially available ITO-coated glass sheet.

[0039] Over the ITO is deposited a hole injecting layer 7 formed from a solution containing poly(ethylene dioxythiophene)/polystyrene sulfonate (PEDOT:PSS) with a PEDOT:PSS ratio of around 1:5. The thickness of the hole transport layer is around 500 Å. The hole transport layer is spin-coated from solution and then baked at around 200° C. for 1 hour in a nitrogen environment.

[0040] Then the electroluminescent material 8 is deposited. Monochrome red and green devices according to the invention, hereinafter referred to as the red device and green device respectively, were prepared in accordance with this example wherein the electroluminescent layers are as follows:

[0041] Red device: blend of F8BT, TFB and Red

[0042] Green device: blend of Host and F8BT

[0043] F8BT=poly(2,7-(9,9-di-n-octylfluorene)-co-3,6-benzothiadiazole)

[0044] TFB=poly(2,7-(9,9-di-n-octylfluorene)-co-(1,4-phenylene-((4-sec-butylphenyl)amino)-1,4-phenylene)

[0045] Red=poly(2,7-(9,9-di-n-octylfluorene)-co-(2,5-thienylene-3,6-benzothiadiazole-2,5-thienylene)

[0046] Host=random copolymer of 90% 2,7-(9,9-di-n-octylfluorene) and 10% 1,4-phenylene-((4-sec-butylphenyl)amino)-1,4-phenylene

[0047] The preparation of these materials is disclosed in WO 99/54385, WO 00/46321 and WO 00/55927, the contents of which are incorporated herein by reference.

[0048] In order to assess the suitability of this device architecture for a full colour display, an analogous blue device was also prepared wherein the electroluminescent layer comprises a random copolymer of poly(2,7-(9,9-di-n-octylfluorene), 1,4-phenylene-((4-sec-butylphenyl)amino)-1,4-phenylene and 1,4-phenylene-((4-n-butylphenyl)amino)-1,4-phenylene-((4-n-butylphenyl)amino)-1,4-phenylene.

[0049] The electroluminescent material for these monochrome devices is spin-coated to a thickness of around 750 Å.

[0050] The electron transporting layer 9 comprising barium is then deposited by evaporation to a thickness of around 4 nm followed by formation of the cathode 10 by evaporation of a calcium layer 11 to a thickness of around 15 Å and a layer of aluminium 12 to a thickness of around 4000 Å. Preferably the vacuum is not broken between evaporation of successive layers to reduce contamination of the interfaces between layers. If a dielectric material such as barium fluoride is to be deposited, evaporation of this material at least is preferably done at a very low rate: preferably less than 1 Å/s, although somewhat higher rates could be used. Preferably, before the material of each cathode layer is deposited it is outgassed by being held at an elevated temperature below its evaporation point—conveniently around 650 to 670° C.—for around 5 to 10 minutes.

[0051] A power supply is connected between the anode 6 and layer 12 of the cathode 10. The power supply is arranged to apply a voltage between the electrodes so as to make cathode 10 electrically negative with respect to anode 6.

[0052] Finally, the device is encapsulated with an epoxy resin.

[0053] B) Full Colour Electroluminescent Device

[0054] A full colour display display device according to the invention may be prepared in accordance with the method outlined above except that the device comprises red, green and blue electroluminescent materials which are advantageously deposited by an inkjet printing process rather than by spin coating as disclosed in, for example, EP 0880303.

[0055] Device Performance

[0056] Performance of red, green and blue monochrome devices comprising a barium fluoride/calcium/aluminium cathode was compared with the performance of devices comprising prior art cathodes lithium fluoride/calcium/aluminium and calcium/aluminium. Through these comparisons, the present inventors have found that use of an electron transport layer comprising barium apparently does not result in the deleterious interactions with the electroluminescent layers comprising sulfur that electron transport layers comprising lithium are prone to.

[0057] Comparative devices were prepared in accordance with the monochrome device examples outlined above except that electron transporting layer 9 comprising barium fluoride was either replaced with lithium fluoride or not deposited at all.

[0058]FIGS. 3 and 4 show comparative plots of current density vs. bias for, respectively, the red device and green device. This illustrates the bias required for device operation—as can be seen, devices according to the invention show similar performance to the comparative devices. The same comparative data for a blue device also showed comparable performance with the three cathodes.

[0059]FIGS. 5 and 6 show the luminance over time for the red device and green device and FIG. 7 shows the same data for the blue device. As can be seen from FIG. 5, the luminance over time of red devices having a barium fluoride/calcium/aluminium is superior to that of red devices with a lithium fluoride/calcium/aluminium cathode or a calcium/aluminium cathode. The difference between the device according to the invention with a barium fluoride/calcium/aluminium cathode and the comparative device with a lithium fluoride/calcium/aluminium cathode is particularly marked. In addition, FIG. 7 shows that a device having a calcium/aluminium cathode shows particularly poor lifetime when used with the blue emissive material whereas devices having the barium fluoride/calcium/aluminium cathode do not show any particular weakness.

[0060] Furthermore, it has been established that performance of the green and, especially, the red devices (i.e. devices with organic electroluminescent layers comprising sulfur) having a lithium fluoride/calcium/aluminium cathode show a very significant fall in lifetime when left in an off state for any length of time. By comparison, it has been found that the lifetime of the red and the green devices having a barium fluoride/calcium/aluminium cathode remains constant regardless of whether they are driven constantly or left in an off state for a length of time.

[0061] Elemental barium has also been employed as the electron transport layer, for example in combination with a layer of silver as the cathode, and has been found to possess essentially the same advantages as a barium fluoride electron transport layer over devices not containing barium, as outlined above.

[0062] Without wishing to be bound by any theory, it is believed that lithium may be able to migrate into the electroluminescent material and bind to sulfur containing species, thus quenching the electroluminescence of these species whereas the larger barium atom or ion is much less capable of such migration.

[0063] Although the present invention has been described in terms of specific exemplary embodiments, it will be appreciated that various modifications, alterations and/or combinations of features disclosed herein will be apparent to those skilled in the art without departing from the spirit and scope of the invention as set forth in the following claims. 

1. An optical device comprising an anode; a cathode; an organic semiconducting material between the anode and the cathode; and, an electron transport layer between the cathode and the organic semiconducting material, wherein the organic semiconducting material comprises sulfur and the electron transport layer comprises barium.
 2. An optical device comprising an anode, a cathode, red, green, and blue electroluminescent organic semiconducting materials located between the anode and the cathode, and an electron transport layer located between the electroluminescent semiconducting materials and the cathode, wherein the electron transport layer comprises barium.
 3. An optical device according to claim 1, wherein the electron transport layer comprises elemental barium as a major component.
 4. An optical device according to claim 1, wherein the electron transport layer comprises a dielectric barium compound as a major component.
 5. An optical device according to claim 4, wherein the dielectric barium compound is barium fluoride.
 6. An optical device according to claim 1, wherein the semiconducting material is a polymer.
 7. An optical device according to claim 6, wherein the polymer comprises optionally substituted polyfluorene repeat units.
 8. An optical device according to claim 1, wherein the semiconducting material comprises a sulfur containing heterocyclic repeat unit.
 9. An optical device according to claim 8, wherein the heterocyclic repeat unit is selected from the group consisting of optionally substituted 4,7-linked benzothiadiazole, 2,5-linked thiophene, and combinations thereof.
 10. An optical device according to claim 1, wherein the organic semiconducting material is a red organic electroluminescent material.
 11. An optical device according to claim 1, wherein the organic semiconducting material is a green organic electroluminescent material.
 12. An optical device according to claim 10 comprising red, green, and blue organic electroluminescent materials between the anode and the electron transport layer.
 13. An optical according to claim 1, wherein the layer comprising barium has a thickness in the range of 1 nm to 6 nm.
 14. An optical device according to claim 1, wherein the cathode comprises a layer of aluminum.
 15. An optical device according to claim 14, wherein the layer of aluminum has a thickness in the range of 200 nm to 700 nm.
 16. An optical device according to claim 14, wherein the cathode comprises a layer of calcium between the electron transport layer and the layer of aluminum.
 17. An optical device according to claim 16, wherein the layer of calcium has a thickness of 5 Å to 25 Å.
 18. An optical device according to claim 1, wherein a hole injecting layer comprising PEDOT:PSS is located between the anode and the semiconducting material.
 19. (Canceled)
 20. An optical device according to claim 2, wherein the electron transport layer comprises elemental barium as a major component.
 21. An optical device according to claim 2, wherein the electron transport layer comprises a dielectric barium compound as a major component.
 22. An optical device according to claim 21, wherein the dielectric barium compound is barium fluoride.
 23. An optical device according to claim 2, wherein the semiconducting material is a polymer.
 24. An optical device according to claim 23, wherein the polymer comprises optionally substituted polyfluorene repeat units.
 25. An optical device according to claim 2, wherein the semiconducting material comprises a sulfur containing heterocyclic repeat unit.
 26. An optical device according to claim 25, wherein the heterocyclic repeat unit is selected from the group consisting of optionally substituted 4,7-linked benzothiadiazole, 2,5-linked thiophene, and combinations thereof.
 27. An optical device according to claim 2, wherein the organic semiconducting material is a red organic electroluminescent material.
 28. An optical device according to claim 2, wherein the organic semiconducting material is a green organic electroluminescent material.
 29. An optical device according to claim 27 comprising red, green, and blue organic electroluminescent materials between the anode and the electron transport layer.
 30. An optical according to claim 2, wherein the layer comprising barium has a thickness in the range of 1 nm to 6 nm.
 31. An optical device according to claim 2, wherein the cathode comprises a layer of aluminum.
 32. An optical device according to claim 31, wherein the layer of aluminum has a thickness in the range of 200 nm to 700 nm.
 33. An optical device according to claim 31, wherein the cathode comprises a layer of calcium between the electron transport layer and the layer of aluminum.
 34. An optical device according to claim 33, wherein the layer of calcium has a thickness of 5 Å to 25 Å.
 35. An optical device according to claim 2, wherein a hole injecting layer comprising PEDOT:PSS is located between the anode and the semiconducting material. 